310S Stainless hlau
Austenitic chromium-nickel stainless hlau 310S pom zoo oxidation thiab corrosion kuj. 310S muaj qhov muaj zog nkag tau zoo heev thiab tuaj yeem ua haujlwm ntawm qhov kub thiab txias vim tias qhov sib piv ntau dua ntawm chromium thiab npib tsib xee. Nws kuj muaj qhov zoo resilience rau qhov kub thiab txias. Vim muaj cov ntsiab lus Ni thiab Cr siab, cov yeeb nkab uas kub kub yog siv los ua hluav taws xob cua sov rauv rauv thiab lwm yam khoom vim nws muaj kev tiv thaiv zoo rau oxidation, corrosion, acid, thiab alkali.
Chemical Composition (%) ntawm 310S Stainless Hlau
| CHEMICAL COMPOSITION (%) | |||||||
| C, max | Mn, mas | P, max | S, max | Si, max | Cr | Ni | Fe |
| 0.08 | 2.00 | 0.045 | 0.030 | 1.50 | 24.00-26.00 | 19.00-22.00 | So |
Mechanical Properties ntawm 310S Stainless hlau
| MECHANICAL PROPERTIES | |||
| Tensile zog, MPa, min | Yield zog, MPa, min | Elongation (%), min | Hardness, max |
| 515 | 205 | 35 | 187 HB |
Lub cev muaj zog ntawm 310S Stainless Hlau
| Lub cev muaj zog | ||||||
| Qhov ntom | Melting Point | Modulus ntawm Elasticity | Tshwj xeeb kub | Hluav taws xob Resistivity | Thermal conductivity | Poisson tus ratio |
| 7.98 g/m² | 1354-1402 degree [2470-2555 degree F] | 196 gpa ua | 502 J/KG | 0.78 μΩ·m | 10.8 W/m.K | 0.30 |
Qib sib npaug ntawm 310S Stainless Hlau
| Qib | JIS | DIN | GB |
| 310S | SUS 310 S | 1.4951 | 06 Cr25Ni20 |
Cov yam ntxwv ntawm 310S Stainless hlau
-Cov cuab yeej kub kub zoo heev
-Zoo ductility thiab weldability
-Khoom corrosion kuj
-Zoo heev oxidation tsis kam
-Lub zog zoo heev
-Zoo heev tsis kam mus creep thiab ib puag ncig erosion
-Zoo kub tsis kam
Daim ntawv thov ntawm 310S Stainless hlau
Siv rau hauv roj av, hluav taws xob, tshuaj, tshuaj, khoom noj, tshuab, kev tsim kho, aerospace, tub rog, thiab lwm yam lag luam.